Factory direct wholesale and retail: TC4 titanium with Ti-6Al-4V titanium belt to ensure quality
Details
The input text or the titanium alloy TC4 material composition is Ti-6Al-4V, belongs to (a+b) type titanium alloy, has the good comprehensive mechanical properties. Specific strength. The strength of sb=1.012GPa, TC4, g=4.4*103, sb/g=23.5, and sb/g, but the strength of the alloy steel is less than 18. Low thermal conductivity of titanium alloy. The thermal conductivity of 1/5, 1/10, l=7.955W/m,, K,, and TC4, the thermal conductivity of titanium alloy. Linear expansion coefficient =7.89*10-6, specific heat =0.612cal/g. The elastic modulus of titanium alloy is lower. The elastic modulus of E=110GPa is about TC4, which is about 1/2, so it is easy to produce deformation during machining. TC4 (Ti-6Al-4V) and TA7 (Ti-5Al-2.5Sn) titanium alloy, the surface modification was carried out with two kinds of injection. The results show that the friction coefficient and the wear resistance can be improved effectively by ion implantation. The satisfactory results are obtained by X ray photoelectron spectroscopy (XPS) analysis.
The thermal expansion coefficient of TC4:
TC4 titanium alloy has a series of advantages, such as excellent corrosion resistance, small density, high specific strength, good toughness and welding, etc., in aerospace, petrochemical, shipbuilding, automobile, medicine and other departments have been successfully applied.
The mechanical properties of TC4 titanium alloy:
The ultimate tensile strength of b/MPa is greater than or equal to 895, specified residual elongation stress r0.2/MPa = 825, 5 elongation (%) = 10, section shrinkage (%) = 25 PSI
The density of TC4 titanium alloy:
4.5 (g/cm3) operating temperature -100 ~ 550 (c)
The chemical composition of TC4 titanium alloy:
TC4 titanium (TI) allowance, and iron (FE) is equal to or less than 0.30, carbon (c) is less than 0.10, the nitrogen (n) is less than or equal to 0.05, hydrogen (H) is less than or equal to 0.015, oxygen (o) is less than or equal to 0.20, aluminum (AL) 5.5 ~ 6.8, vanadium (V) 3.5 ~ 4.5
Can be translated
Factory direct wholesale and retail: TC4 titanium with Ti-6Al-4V titanium belt to ensure quality
Chemical Composition of Titanium Alloy
<^rade of titanium ^ Titanium-Alloy Electrodes & Rods (GUrt ASTiM others) |
Chemical Composition FractionV% |
||||||||||||||||||
Element |
Residuals, Max |
||||||||||||||||||
■Xi |
C |
o |
N |
H |
Fe |
A1 |
V |
Pd |
Ru |
Ni |
Mo |
Ce |
Zr |
Nb |
|
Co |
|
||
AWS Classification |
IONS Number |
||||||||||||||||||
ERTi-1 |
K50100 |
Balance |
0.02 |
0.02-0.10 |
0.012 |
0.005 |
0.08 |
|
|
|
|
|
|
|
|
|
|
|
|
ERTi-2 |
k120 |
Balance |
o.oi |
0.08-0.16 |
0.015 |
0.008 |
0.12 |
|
|
|
|
|
|
|
|
|
|
|
|
i-3 |
K50125 |
Balauoe |
0.02 |
o.n-o.20 |
0.02 |
|
0.16 |
|
|
|
|
|
|
|
|
|
|
|
|
EJifi-4 |
k130 |
Balauoe |
0.02 |
0.18-0-i2 |
0.025 |
|
0.25 |
|
|
|
|
|
|
|
|
|
|
|
|
EJifi-5 |
K56402 |
Balauoe |
0.05 |
0.12-0.20 |
0.02 |
0.015 |
0.22 |
5.S-6.75 |
15-4.5 |
|
|
|
|
|
|
|
|
|
|
i-7 |
K52401 |
Balauoe |
0.02 |
0.08-0. If; |
0.015 |
|
0.12 |
|
|
0.12-0.25 |
|
|
|
|
|
|
|
|
|
ERtiER1i-$ELI |
K56321 |
Balauoe |
0.02 |
0.06-0.12 |
0.012 |
0.005 |
02 |
2.5-15 |
2.0-2.0 |
|
|
|
|
|
|
|
|
|
|
ERH-11 |
R52251 |
Balauoe |
0.02 |
0.02-0.10 |
0.012 |
0.005 |
0.0S |
|
|
0.12-0.25 |
|
|
|
|
|
|
|
|
|
ERH-12 |
K53401 |
Balauoe |
0.02 |
0.08-0. If; |
0.015 |
|
0.05 |
|
|
|
|
0.6-0.9 |
0.2-0.4 |
|
|
|
|
|
|
ERH-13 |
K53423 |
Balauoe |
0.02 |
0.02-0.10 |
0.012 |
0.005 |
0.0S |
|
|
|
0.04-0.06 |
0.4-0 .£; |
|
|
|
|
|
|
|
ERH-14 |
R53424 |
Balauoe |
0.02 |
0.08-0. If; |
0.015 |
|
0.12 |
|
|
|
0.04-0.06 |
0.4-0 .£; |
|
|
|
|
|
|
|
ER11-15A |
K53416 |
Balauoe |
0.02 |
0.12-0.20 |
0.02 |
|
0.16 |
|
|
|
0.04-0.06 |
0.4-0 .£; |
|
|
|
|
|
|
|
|
K52403 |
Balauoe |
0.02 |
0.08-0. If; |
0.015 |
|
0.12 |
|
|
0.04-0.08 |
|
|
|
|
|
|
|
|
|
ERTi-17 |
K52253 |
Balauoe |
0.02 |
0.02-0.10 |
0.012 |
0.005 |
0.0S |
|
|
0.04-0.08 |
|
|
|
|
|
|
|
|
|
ERH-1S |
K56326 |
Balauoe |
0.02 |
0.06-0.12 |
0.012 |
0.005 |
0.20 |
2.5-15 |
2.0-2.0 |
0.04-0.08 |
|
|
|
|
|
|
|
|
|
ERH-1!) |
K641 |
Balauoe |
0.02 |
0.06-0.10 |
0.015 |
0.015 |
0.20 |
2.0-4.0 |
7.S-S.S |
|
|
|
2.S-4.5 |
S.S-6.S |
15-4.5 |
|
|
|
|
ERH-20 |
K6 |
Balauoe |
0.02 |
0.06-0.10 |
0.015 |
0.015 |
0.20 |
2.0-4.0 |
7.S-S.S |
0.04-0.08 |
|
|
2.S-4.5 |
S.S-6.S |
15-4.5 |
|
|
|
|
ERH-21 |
K5S2U |
Balauoe |
0.02 |
0.10-0.15 |
0.012 |
0.005 |
0.20-0.40 |
2.5-15 |
|
|
|
|
14.0-16.0 |
|
|
2.2-12 |
0.15-0.25 |
|
|
ERH-23 |
K5640S |
Balauoe |
0.02 |
0.02-0.11 |
0.012 |
0.005 |
0.20 |
S.S-6.S |
15-4.5 |
|
|
|
|
|
|
|
|
|
|
ERH-24 |
R56415 |
Balauoe |
0.05 |
0.12-0.20 |
0.02 |
0.015 |
0.22 |
5.S-6.75 |
15-4.5 |
0.04-0.08 |
|
|
|
|
|
|
|
|
|
ERH-25 |
R5640 |
Balauoe |
0.05 |
0.12-0.20 |
0.02 |
0.015 |
0.22 |
5.S-6.75 |
15-4.5 |
0.04-0.08 |
|
0.2-0.S |
|
|
|
|
|
|
|
|
R52405 |
Balauoe |
0.02 |
0.08-0. If; |
0.015 |
|
0.12 |
|
|
|
0.08-0.14 |
|
|
|
|
|
|
|
|
ERTi-27 |
R5225S |
Balauoe |
0.02 |
0.02-0.10 |
0.012 |
0.005 |
0.0S |
|
|
|
0.08-0.14 |
|
|
|
|
|
|
|
|
ERH-2S |
R56324 |
Balauoe |
0.02 |
0.06-0.12 |
0.012 |
0.005 |
0.20 |
2.5-15 |
2.0-2.0 |
|
0.08-0.14 |
|
|
|
|
|
|
|
|
ERH-2!) |
R56414 |
Balauoe |
0.02 |
0.02-0.11 |
0.012 |
0.005 |
0.20 |
S.S-6.S |
15-4.5 |
|
0.08-0.14 |
|
|
|
|
|
|
|
|
ERH-30 |
R53531 |
Balauoe |
0.02 |
0.08-0. If; |
0.015 |
|
0.12 |
|
|
0.04-0.08 |
|
|
|
|
|
|
|
020-0.SO |
|
ERH-31 |
R53533 |
Balauoe |
0.02 |
0.12-0.20 |
0.02 |
|
0.16 |
|
|
0.04-0.08 |
|
|
|
|
|
|
|
020-0.SO |
|
ERH-32 |
R55112 |
Balauoe |
0.02 |
0.05-0.10 |
0.012 |
|
0.20 |
4.5-5.5 |
0.6-1.4 |
|
|
|
0.6-12 |
|
0.6-1 A |
|
0.06-0.14 |
|
0.6-1 A |
ERH-33 |
R53443 |
Balauoe |
0.02 |
0.08-0. If: |
0.015 |
|
0.12 |
|
|
0.01-0.02 |
0.02-0.04 |
O^S-O.55 |
|
0.1-0.2 |
|
|
|
|
|
ERH-34 |
R53444 |
Balauoe |
0.02 |
0.12-0.20 |
0.02 |
|
0.16 |
|
|
0.01-0.02 |
0.02-0.04 |
O^S-O.55 |
|
0.1-0.2 |
|
|
|
|
|
ERll-36 |
451 |
Balauoe |
0.02 |
0.06-0.12 |
0.02 |
0.0025 |
0.02 |
|
|
|
|
|
|
|
|
42.0-47.0 |
|
|
|
ERH-3S |
R52451 |
Balauoe |
0.05 |
0.20-0.27 |
0.02 |
0.010 |
1.2-1.S |
2.5-4.S |
2.0-2.0 |
|
|
|
|
|
|
|
|
|
|
|
|
Chemical Composition (Mass Fraction)/% |
|||||||||||||||
Grade of "Titanium Alloy 〇4p alloy {GByl1 ASTM others) |
Nominal |
Element |
Impurity {Max.) |
||||||||||||||
Chemical ComposLtion |
1i |
Al |
&i |
Mo |
|
Cr |
Mn |
Cu |
Si |
Fe |
|
N |
H |
|
Residuals, Max. |
||
|
|
|
|
|
£adi |
total |
|||||||||||
"TCI Orr‘1 |
Ti-2Al-1.5MD |
Balanoe |
1.0~2.5 |
|
|
|
|
0.7~2.0 |
|
|
0.20 |
0.08 |
0.05 |
0.012 |
0.15 |
0.10 |
0.40 |
1C2 cm |
Ti-4Al-1.5MD |
Ealaiioe |
i. 5-5.0 |
|
|
|
|
0.8-2.0 |
|
|
0.20 |
0.08 |
0.05 |
0.012 |
0.15 |
0.10 |
0.40 |
tC3 |
Ti-5A1-4V |
Ealaiioe |
4.5-6.0 |
|
|
2.5-4.5 |
|
|
|
|
0.20 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.40 |
1C4 Gr5 R45400 |
Ti-6A1-4V |
Ealaiioe |
5.5-6.75 |
|
|
2.5-4.5 |
|
CV: 0.005) |
|
|
0.20 |
0.08 |
0.05 |
0.015 |
0.20 |
0.10 |
0.40 |
tC4ELI GrSELI R56407 Q^23 |
Ti-fiAl^tVEU |
Ealaiioe |
5.5-6.5 |
|
|
2.5-4.5 |
|
CV: 0.005) |
|
|
0.25 |
0.08 |
O.ftJ |
0.012 |
0.12 |
0.10 |
0.30 |
tC6 Bt3-1 |
Ti-6 Al-1.5Cr-2.5M〇-0. SFc^O 3Si |
Eslauoe |
5.5-7.0 |
|
2.0-2.0 |
|
0.8-2.2 |
|
|
0.1S-0.40 |
0.2-0.7 |
0.08 |
0.05 |
0.015 |
0.18 |
0.10 |
0.40 |
tCS M'S |
Ti-6.5Al-2.5M^025Si |
Ealaiioe |
5.8-6.8 |
|
2.S-2.8 |
|
|
|
|
0.20-0.25 |
0.40 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.40 |
|
Ti-6.5A1-2 .SU^2,5Sn-0 .iSi |
Ealaiioe |
5.8-6.8 |
1.8-2.8 |
2.S-2.8 |
|
|
|
|
0.20-0.40 |
0.40 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.40 |
1C10 R5<62〇 H-662 |
Ti-6Al-6V-2Sn |
Ealaiioe |
5.5-6.5 |
1.5-2.5 |
|
5.5-6.5 |
|
|
0.25-1.0 |
|
0.25-1.00 |
0.08 |
0.04 |
0.015 |
0.20 |
0.10 |
0.40 |
Grade of "TitBrnum Alloy 〇4p alloy (GB/l1 AS1M others) |
Nominal Chemical Composition |
Chemical Composition (Mass Fraction)/% |
|||||||||||||||
Element |
Impurity {Max.) |
||||||||||||||||
1i |
Al |
&i |
Mo |
V |
Cr |
Zr |
Nb |
Si |
Fe |
C |
N |
H |
o |
Residuals, Max. |
|||
£adi |
total |
||||||||||||||||
icii |
Ti-6.5 Al-2.5fcfo-1.52i--0.2Si |
Eslauoe |
5.8-7.0 |
|
2.S-2.8 |
|
|
0.8-2.0 |
|
0.2-0.25 |
0.25 |
0.08 |
0.05 |
0.012 |
0.15 |
0.10 |
0.40 |
1C12 |
Ti- 5Al-4MD-4〇r-22r-2Sn- lNb |
Ealaiioe |
4.5-5.5 |
1.5-2.5 |
2.S-4.S |
|
15-4.5 |
1.5-10 |
0.5~1.5 |
|
0.20 |
0.08 |
0.05 |
0.015 |
0.20 |
0.10 |
0.40 |
1C15 |
Ti-5Al-2.5Fe |
Ealaiioe |
4.5-5.5 |
|
|
|
|
|
|
|
2.0-2.0 |
0.08 |
0.05 |
0.012 |
0.20 |
0.10 |
0.40 |
tci6 m6 |
Ti-2A1-5M^4.5V |
Ealaiioe |
2.2-18 |
|
4.S-5.S |
4.0-5.0 |
|
|
|
名 0.15 |
0.25 |
0.08 |
0.05 |
0.012 |
0.15 |
0.10 |
0.30 |
1C17 R52252 ^i-17 |
Ti-5Al-2Sn-22r-4Mo-4Cr |
Eslauoe |
4.S-.5 |
1_5~2_5 |
2.S-4.S |
|
|
1.5-2.5 |
|
|
0.25 |
0.05 |
0.05 |
0.0125 |
0.08-0.12 |
0.10 |
0.30 |
1C1S M-22 |
Ti- 5 Al-4,75Mo-4.7 5 V-1 Cr-1 Fe |
Ealaiioe |
4.4~5.7 |
|
4.0-5.5 |
4.0-5.5 |
0.5-1. S |
^0.20 |
|
名 0.15 |
O.S-1.5 |
0.08 |
0.05 |
0.015 |
0.18 |
0.10 |
0.30 |
1C19 R5<2<0 fi-6246 |
Ti-6Al-2Sn-42r-6Mo |
Ealaiioe |
5.5-6.5 |
1.75-2.25 |
5.5-6.5 |
|
|
15-4.5 |
|
|
0.15 |
0.04 |
0.04 |
0.0125 |
0.15 |
0.10 |
0.40 |
tC2〇 R5<700 1MI3<7 |
Ti-6Al-7Nb |
Ealaiioe |
5.5-6.5 |
|
|
|
|
|
6.5^75 |
Ta ^0.5 |
0.25 |
0.08 |
0.05 |
0.009 |
0.20 |
0.10 |
0.40 |
1C21 {CH-62222S) |
Ti-6Al-2fcfo-1.5Cr-22r-2Su-2Nb |
Eslauoe |
5.2-6.8 |
1.6-2.5 |
2.2-23 |
|
0.9-2.0 |
1.6-2.5 |
1.7-23 |
|
0.15 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.40 |
t〇22 Gr24 |
Ti-6Al-4 V-0 ,〇5Pd {Ti-6 A1-4VSTA) |
Ealaiioe |
5.5-6.75 |
|
|
2.5-4.5 |
|
CV: 0.005) |
Pd: 0.04-0.08 |
0.40(0.20) |
0.08 |
0.05 |
0.015(0.0125) |
0.20 |
0.10 |
0.40 |
|
1C23 Gr29 R56404 |
Ti-6Al-4V-0.lRu |
Ealaiioe |
5.5-6.75 |
|
|
2.5-4.5 |
|
|
Ru: 0.08-0.14 |
0.25 |
0.08 |
0.05 |
0.015 |
0.12 |
0.10 |
0.40 |
|
1C24 1i-4322 SP-700 |
Ti-4.5Al-2V-2Mo-2Fe |
Ealaiioe |
4.0-5.0 |
|
l.S-22 |
2.5~15 |
|
|
|
|
1.7-2.3 |
0.05 |
0.05 |
0.010 |
0.15 |
0.10 |
0.40 |
1C25 M-25 |
Ti-6.5 Al-2Mo-l 2r-1 Sd- 1 W-0.2Si |
Ealaiioe |
6.2~7.2 |
0.8-2.5 |
1.S-2.S |
|
W: 0.5-1.5 |
0.8-2.5 |
|
0.10-0.25 |
0.15 |
0.10 |
0.04 |
0.012 |
0.15 |
0.10 |
0.30 |
tCZ6 |
Ti-l2NM22r |
Ealaiioe |
|
|
|
|
|
12.5-14.0 |
12.5-14.0 |
|
0.25 |
0.08 |
0.05 |
0.012 |
0.15 |
0.10 |
0.40 |
Grade of Titanium Alloy {GBAf A^M odiers) |
Nominal Chemical Composition |
Chemical Comp<xsLfion{Mass JVacfion)/% |
||||||||||||||
Element |
Impurity (Max.) |
|||||||||||||||
1i |
A1 |
Mo |
V |
Mn |
Zr |
Si |
Nd |
Fe |
C |
N |
H |
o |
Residuals, Max. |
|||
Each |
total |
|||||||||||||||
TA20 (CITT-2) |
Ti-4Al-2V-1.52r |
Balance |
i.S-4.5 |
|
2.5-15 |
|
l.ft-2.0 |
0.10 |
|
0.15 |
0.05 |
0.04 |
0.002 |
0.12 |
0.10 |
0.30 |
TA21 {0t4-0) |
Ti-lAl-lMn |
Balaircc |
0.4-1.5 |
|
|
0.S-1.2 |
^020 |
0.12 |
|
0.30 |
0.10 |
0.05 |
0.012 |
0.15 |
0.10 |
0.20 |
1A22 CIi-31) |
Ti-2Al-lMo-lNi-l2r |
Balaircc |
2.S-2.5 |
0.5-1.5 |
Ni: 03-1.0 |
0.8-2.0 |
0.15 |
|
0.20 |
0.10 |
0.05 |
0.015 |
0.15 |
0.10 |
0.20 |
|
TA22-1 C^IA) |
Ti-2Al-lMo-lNi-l2r |
Balaircc |
2.S-2.5 |
0.2-0.8 |
Ni: 03-0.8 |
0.S-1.0 |
0.04 |
|
0.20 |
0.10 |
0.04 |
0.008 |
0.10 |
0.10 |
0.20 |
|
1A23 CH-70) |
Ti-2.5Al-22r-lFe |
Balaircc |
2.2-2.0 |
|
Ni: 0.8-1.2 |
1.7-2.2 |
0.15 |
|
|
0.10 |
0.04 |
0.010 |
0.15 |
0.10 |
0.20 |
|
TA23-1 C^-7〇A) |
Ti-2.5Al-22r-lFe |
Balaircc |
2.2-2.0 |
|
Ni: 0.8-1.1 |
1.7-2.2 |
0.10 |
|
|
0.10 |
0.04 |
0.008 |
0.10 |
0.10 |
0.20 |
|
1A24 CIi-75) |
Ti-iAl-2fcfo-22r |
Balaircc |
2.S-2.5 |
1.0-2.5 |
|
1.0-2.0 |
0.15 |
|
0.30 |
0.10 |
0.05 |
0.015 |
0.15 |
0.10 |
0.20 |
|
1A24-1 C^-^SA) |
Ti-iAl-2fcfo-22r |
Balaircc |
l.S-2.5 |
1.0-2.0 |
|
1.0-2.0 |
0.04 |
|
0.15 |
0.10 |
0.04 |
0.010 |
0.10 |
0.10 |
0.20 |
|
tA25 GrlS |
Ti-iAl-2.5V-0.05f>d |
Balaircc |
2.S-2.5 |
|
2.0-10 |
|
|
M 0.04-0.08 |
0.25 |
0.08 |
O.ftJ |
0.015 |
0.15 |
0.10 |
0.40 |
|
tA26 Gr25 R56323 |
Ti-iAl-2.5V-0.lRu |
Balaircc |
2.S-2.5 |
|
2.0-10 |
|
|
Ru: 0.0S-0.14 |
0.25 |
0.08 |
O.ftJ |
0.015 |
0.15 |
0.10 |
0.40 |
|
1A27 Gr2-6 R52404 |
Ti-0.10Ru |
Balaircc |
|
|
Ru: 0.08-0.14 |
|
|
|
0.20 |
0.08 |
O.ftJ |
0.015 |
0.25 |
0.10 |
0.40 |
|
1A27-1 Gr27 |
Ti-0.10Ru |
Balaircc |
|
|
Ru: 0.08-0.14 |
|
|
|
0.20 |
0.08 |
O.ftJ |
0.015 |
0.18 |
0.10 |
0.40 |
|
1A2S |
Ti-iAl |
Balaircc |
2.0-2.0 |
|
|
|
|
|
0.30 |
0.08 |
O.ftJ |
0.015 |
0.15 |
0.10 |
0.40 |
Grade of Titanium Alloy p alloy {GBflf ASTMo^icrs) |
Nominal Chemical Compixsition |
Chemical Comp<xsifion(M3ss fVacfioii)/% |
||||||||||||||
Element |
Impurity ^rfax.) |
|||||||||||||||
ti |
A1 |
&i |
Mo |
V |
Cr |
2r |
Pd |
Fe |
C |
N |
H |
o |
Residuals, Max. |
|||
£acb |
total |
|||||||||||||||
r〇2 |
Ti-5Mo-5V-80r-2Al |
Balaircc |
2.S-2.5 |
|
4.7~5.7 |
4.7-S.7 |
7.S-8.5 |
|
|
0.30 |
0.05 |
0.04 |
0.015 |
0.15 |
0.10 |
0.40 |
m3 |
Ti-l5Al-10fcfo-SfV-lFe |
Balaircc |
2.7~i.7 |
|
9.5-11.0 |
7.S-8.5 |
|
|
|
0.8-12 |
0.05 |
0.04 |
0.015 |
0.15 |
0.10 |
0.40 |
1B4 |
Ti-4Al-7M^10V-2F^l2r |
Balaircc |
2.0-4.5 |
|
0-7.8 |
9.0-10.5 |
|
O.S-1.5 |
|
1_5~2_S |
0.05 |
0.04 |
0.015 |
0.20 |
0.10 |
0.40 |
Ti-15-3-3-3 |
Ti-15V-2Al-iCr-2Sii |
Balaircc |
2.S-2.5 |
2.S-2.5 |
|
14.0-16.0 |
2.S-2.5 |
|
|
0.25 |
0.05 |
0.05 |
0.015 |
0.15 |
0.10 |
0.20 |
^6 R56410 1i-l〇23 |
Ti-10V-2F^2Al |
Balaircc |
2.6-2.4 |
|
|
9.0-11.0 |
|
(Y: 0.005) |
|
1.6-2.22 |
0.05 |
0.05 |
0.015 |
0.1 12) |
0.10 |
0.20 |
tB7 H-32 |
Ti-22Mo |
Balaircc |
|
|
20.0-24.0 |
|
|
|
|
0.30 |
0.05 |
0.05 |
0.015 |
0.20 |
0.10 |
0.40 |
|!21s |
Ti-15M^2Al-2.7N^0.2SSi |
Balaircc |
2.S-2.5 |
|
14.0-16.0 |
Nb: 2.4-12 |
Si: 0.1S-0.25 |
0.40 |
0.05 |
0.05 |
0.015 |
0.17 |
0.10 |
0.40 |
||
R5S640 pc |
Ti-iAl-8V-6Cr-4Mo^2r |
Balaircc |
2.0-4.0 |
|
2.5-4.5 |
7.S-8.5 |
5.S-6.5 |
2.S-4.5 |
名 0.10 |
0.30 |
0.05 |
O.ftJ |
O.ftJO |
0.14 |
0.10 |
0.40 |
1U10 CHJ523) |
Ti-5Mo-5V-2Cr-2Al |
Balaircc |
2.S-2.5 |
|
4.5~5.5 |
4.S-5.5 |
l.S-2.5 |
|
|
0.30 |
0.05 |
0.04 |
0.015 |
0.15 |
0.10 |
0.40 |
tBll Ti-15Mo |
Ti-l5Mo |
Balaircc |
|
|
14.0-16.0 |
|
|
|
|
0.10 |
0.10 |
0.05 |
0.015 |
0.20 |
0.10 |
0.40 |
Grade of Yitamum CP Titanium & a alloy {GB/Tf ASTTM IONS others) |
Nominal Chemical Composition |
Chemical Composition (Mass JVactLon)/% |
||||||||||||||
Element |
Impurity |
|||||||||||||||
ti |
A1 |
|
Mo |
Pd |
Ni |
Si |
C |
Fe |
C |
N |
H |
o |
Residuals, Max. |
|||
£adb |
Total |
|||||||||||||||
tAl£LI CrlEO |
CP Titanium |
Balacrcc |
|
|
|
|
|
|
|
0.10 |
o.fti |
0.012 |
0.008 |
0.10 |
0.05 |
0.20 |
1A1 Grl R5ft25〇 Ml-00 |
CP Titanium |
Balazrce |
|
|
|
|
|
|
|
0.20 |
0.08 |
O.ftJ |
0.015 |
0.18 |
0.10 |
0.40 |
tAl-1 Bfl-OOCB |
CP Titanium |
Balance |
名 0.20 |
|
|
|
|
^0.08 |
|
0.15 |
0.05 |
O.ftJ |
0.002 |
0.12 |
|
0.10 |
TA2ELI Gr2ELI |
CP Titanium |
Balaircc |
|
|
|
|
|
|
|
0.20 |
0.05 |
O.ftJ |
0.008 |
0.10 |
0.05 |
0.20 |
1A2 Gr2 R50400 1^2 |
CP Titanium |
Balaircc |
|
|
|
|
|
|
|
0.30 |
0.08 |
O.ftJ |
0.015 |
0.25 |
0.10 |
0.40 |
TA3ELI Gr3ELI |
CP Titanium |
Balaircc |
|
|
|
|
|
|
|
0.25 |
0.05 |
0.04 |
0.008 |
0.18 |
0.05 |
0.20 |
1A3 Gr3 K50550 |
CP Titanium |
Balaircc |
|
|
|
|
|
|
|
0.30 |
0.08 |
0.05 |
0.015 |
0.25 |
0.10 |
0.40 |
TA4ELI Gr4ELI |
CP Titanium |
Balaircc |
|
|
|
|
|
|
|
0.30 |
0.05 |
0.05 |
0.008 |
0.25 |
0.05 |
0.20 |
1A4 Gr4 R50700 |
CP Titanium |
Balaircc |
|
|
|
|
|
|
|
0.50 |
0.08 |
0.05 |
0.015 |
0.40 |
0.10 |
0.40 |
1A5 |
Ti-4A1-0.005B |
Balaircc |
2.>4.7 |
|
|
|
|
|
0.005 |
0.20 |
0.08 |
0.04 |
0.015 |
0.15 |
0.10 |
0.40 |
TAi BTf5 |
Ti-5A1 |
Balaircc |
4.0-5.5 |
|
|
|
|
|
|
0.30 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.40 |
TA7 Gr6 R54520 BT5-1 |
Ti-5Al-2.SSn |
Balaircc |
4.0-6.0 |
2.0-2.0 |
|
|
|
|
|
0.50 |
0.08 |
0.05 |
0.015 |
0.20 |
0.10 |
0.40 |
TA7ELICIA70) R54521 |
Ti-5Al-2.5SnEn |
Balaircc |
4.50-5.75 |
2.0-2.0 |
|
|
|
|
|
0.25 |
0.05 |
0.025 |
0.0125 |
0.12 |
0.05 |
0.30 |
tAS Qrl6 R52402 |
Ti-0.05f>d |
Balaircc |
|
|
|
0.04-0.08 |
|
|
|
0.30 |
0.08 |
O.ftJ |
0.015 |
0.25 |
0.10 |
0.40 |
tAS-1 Grl7 R52252 |
Ti-0.05f>d |
Balaircc |
|
|
|
0.04-0.08 |
|
|
|
0.20 |
0.08 |
O.ftJ |
0.015 |
0.18 |
0.10 |
0.40 |
1A$ Gr7 R52400 |
Ti^.2Pd |
Balaircc |
|
|
|
0.12-0.25 |
|
|
|
0.30 |
0.08 |
O.ftJ |
0.015 |
0.25 |
0.10 |
0.40 |
TA9-1 Grll R52250 |
Ti^.2Pd |
Balaircc |
|
|
|
0.12-0.25 |
|
|
|
0.20 |
0.08 |
O.ftJ |
0.015 |
0.18 |
0.10 |
0.40 |
TA10 Grl2 R53400 |
Ti-03M^0.8Ni |
Balaircc |
|
|
02-0.4 |
|
0.6-0.9 |
|
|
0.30 |
0.08 |
O.ftJ |
0.015 |
0.25 |
0.10 |
0.40 |
Grade of *Htamuin {GBflf A^fMovers) |
Nominal Chemical Compixsition |
Chemical ComjHxsifion (Mass ¥Vaction)/0/〇 |
||||||||||||||
Element |
Impurity |
|||||||||||||||
ti |
A1 |
&i |
Mo |
V |
2r |
Si |
Nd |
Fe |
C |
N |
H |
o |
Residuals, Max. |
|||
£acb |
total |
|||||||||||||||
TAll K54S10 Ti^ll |
Ti-8Al-lfcfo-lV |
Balaircc |
7.25-8.35 |
|
0.75-1.25 |
0.7S-1.25 |
|
|
|
0.30 |
0.08 |
0.05 |
0.015 |
0.12 |
0.10 |
0.30 |
TA12 {Tfi-Sll) |
Ti-5.5A1-4Sd-22t- 1Mo-1 Nd-0,25Si |
Balaircc |
4.S-6.0 |
17-4.7 |
0.75-1.25 |
|
l.S-2.5 |
0.2-0.25 |
0.6-1.2 |
0.25 |
0.08 |
0.05 |
0.0125 |
0.15 |
0.10 |
0.40 |
TA12-1 cn^sn) |
Ti-5.5A1-4Sd-22t- 1Mo-1 Nd-0,25Si |
Balaircc |
4.S-5.5 |
17-4.7 |
1.0-2.0 |
|
l.S-2.5 |
0.2-0.25 |
0.6-1.2 |
0.25 |
0.08 |
0.04 |
0.0125 |
0.15 |
0.10 |
0.30 |
tAB IMI230 |
Ti-2.5Cu |
Balaircc |
Cu: 2.0-2.0 |
|
|
|
|
|
0.20 |
0.08 |
0.05 |
0.010 |
0.20 |
0.10 |
0.30 |
|
tA14 H-679 |
Ti-2.2 Al-11 So- SZx- IMo-0 ,2Si |
Balaircc |
2.ft-2.5 |
10.52-11.5 |
03-1.2 |
|
4.0-6.0 |
0.10-0.50 |
|
0.20 |
0.08 |
0.05 |
0.0125 |
0.20 |
0.10 |
0.30 |
1A1S CT2〇 |
Ti-6.5Al-lM^lV-22r |
Balaircc |
S.S-7.1 |
|
0.5-2.0 |
0.&-2.5 |
l.S-2.5 |
0.15 |
|
0.25 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.30 |
tA15-l I«f20-1CB |
Ti-2.5Al-lM^lV-l.S2r |
Balaircc |
2.0-2.0 |
|
0.5-1. S |
O.S-1.5 |
1.0-2.0 |
0.10 |
|
0.15 |
0.05 |
0.04 |
0.002 |
0.12 |
0.10 |
0.30 |
TA15-2 l«f2〇-2CB |
Ti-4Al-lhfo-lV-1.52r |
Balaircc |
2.S-4.5 |
|
0.5-1. S |
O.S-1.5 |
1.0-2.0 |
0.10 |
|
0.15 |
0.05 |
0.04 |
0.002 |
0.12 |
0.10 |
0.30 |
TA16 ilH-TM) |
Ti-2Al-2.52i |
Balance |
1.8-2.5 |
|
|
|
2.0-10 |
0.12 |
|
0.25 |
0.08 |
0.04 |
0.006 |
0.15 |
0.10 |
0.30 |
1A17 {MtoB) |
Ti-4A1-2V |
Balaircc |
2.S-4.5 |
|
|
1.5-2.0 |
|
0.15 |
|
0.25 |
0.08 |
0.05 |
0.015 |
0.15 |
0.10 |
0.30 |
tAlS Orif R5<632〇 0t4-lB |
Ti-2A1-2.5V |
Balaircc |
2.0-2.5 |
|
|
1.5-2.0 |
|
|
|
0.25 |
0.08 |
0.05 |
0.015 |
0.12 |
0.10 |
0.30 |
TA19 R5462-0 •H-6242S |
Ti-6Al-2Sn^2r-2fcfo |
Balaircc |
5.5-6.5 |
1.&-2.2 |
1.8-2.2 |
CV: 0.005) |
l.^A.4 |
Si: ^0.12(0.06-0.1) |
0.25 |
0.05 |
0.05 |
0.015 |
0.15(0.12) |
0.10 |
0.30 |